Mechanical Performance and Reliability Assessment of Nanosilica-Modified High-Strength Concrete Beams
Ooye Steeve Tobi,
John Wasiu,
Ibrahim Abdulrazaq Olayinka*
,
Osegbowa Douglas Enoguan
Issue:
Volume 15, Issue 3, September 2026
Pages:
80-90
Received:
15 June 2026
Accepted:
26 June 2026
Published:
17 July 2026
DOI:
10.11648/j.am.20261503.11
Downloads:
Views:
Abstract: The growing demand for high-performance and durable construction materials has led to increasing interest in nanotechnology applications in concrete. This study investigates the mechanical properties, microstructural behavior, and structural reliability of high-strength concrete beams (HSCBs) incorporating nanosilica as a partial cement replacement. Experimental investigations were conducted on concrete mixes containing 0%, 3%, 5%, and 7% nanosilica by weight of cement. Material characterization included sieve analysis, specific gravity, water absorption, and density tests for aggregates, while nanosilica was evaluated using SEM/EDX and FTIR to examine its morphology and chemical interactions. Compressive strength tests were performed at 7, 14, 21, and 35 days, and flexural strength tests were conducted on reinforced concrete beams. Results showed significant improvements in both compressive and flexural strengths with nanosilica incorporation, with the optimum performance observed at 5% replacement, achieving up to 18% higher compressive strength than the control mix. Microstructural analysis confirmed enhanced formation of calcium silicate hydrate (C–S–H) gel and pore refinement due to nanosilica’s pozzolanic reactivity and filler effect. Furthermore, structural performance was evaluated using both deterministic design methods and reliability-based analysis (FORM), demonstrating that nanosilica-modified beams achieved higher reliability indices and reduced probabilities of failure. The study concludes that controlled incorporation of nanosilica significantly enhances the strength, durability potential, and structural safety of high-strength concrete beams.
Abstract: The growing demand for high-performance and durable construction materials has led to increasing interest in nanotechnology applications in concrete. This study investigates the mechanical properties, microstructural behavior, and structural reliability of high-strength concrete beams (HSCBs) incorporating nanosilica as a partial cement replacement...
Show More
Research Article
Effect of Precursor Solution Volume on Structural and Optical Properties of Iron Doped Titanium Dioxide Thin Films Prepared by Spin Coating
Chemutai Sharon*,
John Njagi,
Jatani Ungula,
Sharon Kiprotich
Issue:
Volume 15, Issue 3, September 2026
Pages:
91-98
Received:
18 June 2026
Accepted:
1 July 2026
Published:
22 July 2026
DOI:
10.11648/j.am.20261503.12
Downloads:
Views:
Abstract: The influence of precursor solution volume on the characteristics of containing iron-doped titanium dioxide (Fe:TiO2) thin films was examined in this work. The coatings were prepared on transparent substrates by the spin-coating method using precursor volumes between 0.5 and 2.5 mL. Following deposition, the coatings were heat treated at 450°C and analyzed using X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and ultraviolet-visible (UV-Vis) spectroscopy. XRD analysis revealed the presence of both rutile and anatase crystalline phases, evidenced by reflections near 27.4° and 49° corresponding to the (110) and (200) planes, respectively. Variations in precursor volume affected the crystallographic properties of the films, with the sample prepared using 1.0 mL exhibiting the largest crystallite size and sharper diffraction peaks, suggesting improved crystal growth. Increasing the precursor volume beyond this value resulted in peak broadening, which may be associated with greater lattice imperfections and strain within the films. The FTIR results identified characteristic vibrational bands assigned to Ti-O-Ti and Ti-O-Fe linkages, confirming the incorporation of iron species into the TiO2 network. Optical characterization showed that increasing precursor volume shifted the absorption threshold toward longer wavelengths and reduced the optical band gap. This behavior can be ascribed to the creation of defect-induced energy states and oxygen-vacancy states within the material. Overall, the findings demonstrate that precursor solution volume significantly affects both the crystallographic and photonic performance of Fe:TiO2 coatings, with the 1.0 mL sample providing the most favorable combination of crystallinity and film quality.
Abstract: The influence of precursor solution volume on the characteristics of containing iron-doped titanium dioxide (Fe:TiO2) thin films was examined in this work. The coatings were prepared on transparent substrates by the spin-coating method using precursor volumes between 0.5 and 2.5 mL. Following deposition, the coatings were heat treated at 450°C and ...